Maximum percentage of Phosphorous (P) is 0.040 percent. Maximum percentage of Sulphur (S) is 0.040 percent. Remaining is iron (Fe) percentage and with few negligible impurities. BEBON STEEL can offer SAPH440 hot rolled automobile structural plates with available thickness from 3mm to 150mm.
Hot rolled structural steel in JIS standard - JOIN WIN STEELJIS G3113 Hot-rolled Automobile structural steel. Standard:JIS G3113 Steel Grade :SAPH310, SAPH370, SAPH400, SAPH440 Dimension range :1.5mm -20mm x 900mm-2000mm x
How can I determine the 0.2% yield stress from my stress The yield strength at 0.2% offset is determined by finding the intersection of the stress-strain curve with a line parallel to the initial slope of the curve and which intercepts the abscissa at 0.2%.
JIS G3113 SAPH440 steel plate, SAPH440 Automobile structure steel plate, JIS G3113 Automobile structure steel plate ,SAPH440 steel plate is mainly used in automobile industry, produce car frame, wheels and other automotive structural parts with requirement for
JIS G3113 Structural Automobile Hot Rolled SAPH370 SteelJan 25, 2013 · The yield strength is minimum 215 to minimum 225 N/mm2 (MPa) depending on the thickness, lower thickness gauges below 8mm are required with minimum 225 N/mm2 and the higher gauges from 8 mm require 215 N/mm2 minimum yield strength. The elongation property of SAPH370 steel varies with the ranges of thickness.
Jis G3113 Saph440 Automotive Carbon Structural Steel Plate Jis G3113 Saph440 Automotive Carbon Structural Steel Plate , Find Complete Details about Jis G3113 Saph440 Automotive Carbon Structural Steel Plate,Carbon Steel Plate,Carbon Structural Steel Plate,Automotive Structural Steel from Steel Sheets Supplier or Manufacturer-Shandong Jingen International Trading Co., Ltd.
The steel plate SAPH310,SAPH370,SAPH400,SAPH400 are hot rolled mild steel plates with the minimum tensile strength of 310MPa,370MPa,400MPa and 440MPa.
SAPH440 EquivalentJIS G3113 Structural Automobile Hot MECHANICAL PROPERTIES OF SAPH440 STEELS The tensile strength of the SAPH440 Steels is eed in Newton per millimeters and it must be at least 440 N/mm2 (MPa). The yield strength is minimum 275 to minimum 305 N/mm2 (MPa) depending on the thickness. The elongation property of SAPH440 steel varies with the ranges of thickness.
StandardPropertiesofTypical (0.2% OFFSET) YIELD STRENGTH (0.05% OFFSET) EL ROCKWELL HARDNESS VICKENS HARD. BRINELL HARD. SHEAR STRENGTH FATIGUE STRENGTH* IZOD IMPACT STRENGTH in. % F ksi ksi ksi ksi % BC F30T 500 3000 ksi ksi ft-lb mm. C MPa MPa MPa MPa MPa MPa J M01 0.0 0 TYP 68 95 48 20 180 12.0 0.0 20 655 331 20 180 16.0 1. In determining Cu min., Cu may be calculated
The 0.2% offset yield strength (0.2% OYS, 0.2% proof stress, R P0.2, R P0,2) is defined as the amount of stress that will result in a plastic strain of 0.2%. This is illustrated by the blue line in Figure 1 below. This is the yield strength that is most often quoted by material suppliers and JIS G 3113 SAPH440 steel plate steel plate,JIS G 3113 JIS G 3113 SAPH440 steel plate Chemical composition(%) C0.21 Si0.30 Mn1.50 S0.025 P0.025 Al0.010. JIS G 3113 SAPH440 steel plate Mechanical properties(%) Tensile strength Mpa Min:440 Yield strength Mpa:295-305. JIS G 3113 SAPH440 steel plate Specification. Thickness:2-14mm. Width:950-2000mm. Length:1000mm-18000mm. Technique:Hot Rolled